Series 300
Properties
They are RTV-2 silicone rubber, pourable, bi-component and vulcanizing at room-temperature with a poly-addition process. They don’t contain toxic or corrosive substances and so don’t require particular security measures during the storage. High mechanical properties and low viscosity give very flexible and resistant moulds and high details reproduction. They’re suitable to reproduce wax, plaster, resins models.
How to use
Make sure that the model to duplicate is perfectly clean and dry. Before using shake well the bottles of part A and part B. Mix exactly the same quantity (1:1) of part A and part B. If the proportions are not exactly, the curing times and the final properties can be different. Mix about a minute until a homogeneous colour is obtained, then pour the mixture on the model to duplicate. To reduce air bubbles, we suggest a vacuum de-airing treatment before pouring the silicone rubber, compatible with the curing times. The curing speed is influenced by the temperature. We recommend to work in an isothermal place at 23°C. Higher temperatures accelerate the curing times, lower temperatures reduce them. The cured silicone can be demoulded after the time shown on the label (Setting time). In order to reach the best performance of the moulds, we suggest to wait for 24 hours before using them. Some inhibitions to vulcanization process may occur when the silicone rubber get in contact with amines, plasticines, metal salts, sulphur, tin catalyst and poly-condensation silicone rubber. To avoid any inhibition problems, we recommend a preliminary test for the compatibility of the silicone on the material to duplicate. The products, when stored under appropriate conditions, are stable and usable for 12 months. We suggest to keep the products in their original packaging, well-closed at a temperature between +7°C and +27°C, in well-aired places. Close always the bottles after use. Do not reverse the cap.

Our products
FEINGOSIL PA 306 (A+B) for wax, plaster, resins models
Mix ratio: 100:100
Colour: Red
Viscosity: 2.500 mPa∙s
Working time: 30 minutes
Setting time: 2 hours
Hardness 24 h: 5 Shore A
FEINGOSIL PA 312 (A+B) for wax, plaster, resins models
Mix ratio: 100:100
Colour: Orange
Viscosity: 6.500 mPa∙s
Working time: 30 minutes
Setting time: 2 hours
Hardness 24 h: 13 Shore A
FEINGOSIL PA 322 (A+B) for wax, plaster, resin models
Mix ratio: 100:100
Colour: Light Blue
Viscosity: 6.000 mPa∙s
Working time: 60 minutes
Setting time: 4 hours
Hardness 24 h: 22 Shore A
FEINGOSIL PA 325 (A+B) pourable RTV-2 silicone rubber
Mix ratio: 100:100
Colour: Red
Viscosity: 7.000 mPa∙s
Working time: 60 minutes
Setting time: 4 hours
Hardness 24 h: 25 Shore A
FEINGOSIL PA 330 (A+B) bi-component RTV-2 rubber
Mix ratio: 100:100
Colour: Yellow
Viscosity: 7.500 mPa∙s
Working time: 60 minutes
Setting time: 4 hours
Hardness 24 h: 30 Shore A
FEINGOSIL PA 340 (A+B) RTV-2 silicone rubber for jewellery
Mix ratio: 100:100
Colour: Violet
Viscosity: 25.000 mPa∙s
Working time: 30 minutes
Setting time: 4 hours
Hardness 24 h: 40 Shore A
FEINGOSIL PA 345LT (A+B) RTV-2 silicone rubber for circuits
Mix ratio: 100:100
Colour: Light Blue
Viscosity: 6.000 mPa∙s
Working time: 10 minutes
Setting time: 45 ÷ 60 minutes
Hardness 24 h: 43 Shore A
FEINGOSIL PA 350F (A+B) silicone rubber for millable moulds
Mix ratio: 100:100
Colour: Green
Viscosity: 12.000 mPa∙s
Working time: 30 minutes
Setting time: 3 hours
Hardness 24 h: 50 Shore A